Published Paper Details:

Synthesis of Nickel Ferrite, a low-temperature combustion path is used by adding a fossil fuel of 2.360 grams of Nickel Nitrate and Ferrous Nitrate was taken in a ceramic crucible and 15 ml of organic fuel was poured into the crucible and mixed homogeneously. The prepared mixture was put into the preheated muffler furnace, which was kept at 400 0C. In this case, a combustion reaction occurs between metallic nitrates and fuel, producing Nano powders of NiFe2O4.The nanocomposite LDPE thin films were synthesized by dissolving NiFe2O4 NPS of desired quantity for LDPE suspension, and after 60 minutes of ultrasonication 10 ml of each composition is dispersed in a separate glass petri-dishes. All the films were dried at 70 ° C for 60 minutes and kept at room temperature for 48 hr. This is particularly important because the water remaining in the mixture could cause air bubbles to form in the samples. The average crystallite size of LDPE/NiFe2O4 Polymer Nanocomposites is found to be 30 nm by XRD, the prepared samples are Characterized for Mechanical properties and FTIR. Pure LDPE had a high tensile strength and very little elongation at break, whereas composites containing additional Nano particles had a greater tensile strength and much more elongation at break than pure LDPE.